High-Performance Layered CaV4O9-MXene Composite Cathodes for Aqueous Zinc Ion Batteries

Due to their reliability, affordability and high safety, rechargeable aqueous zinc ion batteries (ZIBs) have garnered a lot of attention. Nevertheless, undesirable long-term cycle performance and the inadequate energy density of cathode materials impede the development of ZIBs. Herein, we report a layered CaV4O9-MXene (Ti3C2Tx) composite assembled using CaV4O9 nanosheets on Ti3C2Tx and investigate its electrochemical performance as a new cathode for ZIBs, where CaV4O9 nanosheets attached on the surface of MXene and interlamination create a layered 2D structure, efficiently improving the electrical conductivity of CaV4O9 and avoiding the stacking of MXene nanosheets. The structure also enables fast ion and electron transport. Further discussion is conducted on the effects of adding MXene in various amounts on the morphology and electrochemical properties. The composite shows an improved reversible capacity of 274.3 mA h g−1 at 0.1 A g−1, superior rate capabilities at 7 A g−1, and a high specific capacity of 107.6 mA h g−1 can be delivered after 2000 cycles at a current density of 1 A g−1. The improvement of the electrochemical performance is due to its unique layered structure, high electrical conductivity, and pseudo capacitance behavior.


Introduction
The energy crisis and environmental pollution make the development of large-scale energy storage systems imminent. Lithium-ion batteries (LIBs) dominate the energy storage field of 3C electronics and the electric vehicle industry [1][2][3][4]. Nevertheless, the limited resources of lithium, safety, and high cost dramatically hinder the future sustainability of lithium-ion batteries [5][6][7]. Recently, aqueous zinc ion batteries (ZIBs) with lower cost, higher security, high efficiency, and ultra-high theory capacity (820 mAh g −1 ) have attracted increasing attention [8][9][10]. Yet, achieving high performance aqueous ZIBs with long-term life cycles and high energy density remains a challenge owing to the low electrical conductivity and structural instability of conventional cathode materials [11][12][13][14][15]. Currently, the widely reported cathodes for ZIBs are mainly based on manganese-or vanadium-based oxides, Prussian blue analogs, spinel-structured oxides, and organic materials [5,[16][17][18][19]. Among those materials, vanadium-based materials show promising because of their tremendous natural richness, multiple valence states, and unique layered structure.
Although vanadium-based materials have made great progress in the intercalation/ deintercalation of Zn 2+ , such materials often suffer from slow diffusion kinetics, irreversible phase transitions, and even structural collapse [20,21]. One of the most effective strategies is the introduction of metal ions such as M x V 2 O 5 ·nH 2 O (M = Zn, Ca, Mg). Metal ions in vanadium oxides can enhance the structural stability of the host material, and thus improve the cyclic performance [22,23]. Calcium vanadate (CaV 4 O 9 , CVO), having a typical lamellar structure in which [V 4 O 9 ] 2n− n sheets consist of a VO 5 square pyramid with shared vertices, shows higher conductivity and specific surface area [20,[24][25][26]. The strength of the V-O

Synthesis of Ti 3 C 2 T x MXene
Firstly, 2 g of Ti 3 AlC 2 MAX powder was placed in a plastic beaker containing 20 mL of HF (49 wt%), stirred at ambient temperature for 24 h to etch the Al element in the MAX, then the sample was washed with distilled water to pH = 7 and dried in vacuum at 60 • C for 12 h to collect Ti 3 C 2 T x MXene powder.

Synthesis of CaV 4 O 9 -MXene
1 mmol of Ca(OH) 2 was added to a mixture of 10 mL glycerol and 10 mL water, 2 mmol V 2 O 5 was dispersed in 10 mL of deionized water, then 5 mL H 2 O 2 solution was slowly added. Stirring the two solutions separately for 1 h, afterwards it was stirred for 2 h after mixing; finally, MXene powder was added and stirred for another 2 h. The mixture was placed in a 50 mL polytetrafluoroethylene kettle encapsulated in a stainless-steel reactor and kept at 200 • C for 48 h. After solvothermal reaction, the CaV 4 O 9 -MXene material was obtained using suction filtration, repeated cleaning with distilled water and ethanol, and the material was dried in vacuum for 12 h. For comparison, the samples with different amounts of MXene, including 0.1 g, 0.2 g, 0.3 g, were prepared, and the obtained samples were labeled as CaV 4 O 9 -MXene-0.1, CaV 4 O 9 -MXene-0.2, and CaV 4 O 9 -MXene-0.3, respectively.

Electrochemical Measurements
To prepare the CaV 4 O 9 -MXene cathode, the electrochemical active material (CaV 4 O 9 -MXene) was mixed with ethynyl black and polyphenylene fluoride (PVDF) in N-methyl pyrrolidone in a ratio of 8:1:1 by weight, then the slurry was coated on titanium foil polished with sandpaper, while zinc foil and a glass fiber membrane (GF/D) were applied as the anode and separator, respectively. Deoxygenated 3M Zn (CF 3 SO 3 ) 2 was used as the electrolyte. Subsequently, the cathode was dried in vacuum under 60 • C for 12 h. CR2032 cells were fabricated using as-prepared electrodes in air. The electrochemical properties of the cells were evaluated using a LAND battery test system (CT2001A), including specific capacity, rate performance, and long-term cycling stability. Cyclic voltammetry (CV) measurements were performed on a CHI 760E electrochemical workstation. Contact angle test was performed on a JC 2000D1 contact Angle tester. Figure 1a depicts the preparation process of CaV 4 O 9 -MXene composite. Firstly, MXene was synthesized via a hydrogen fluoride solution etching Al atom from a MAX phase. CaV 4 O 9 nanosheets homogeneously anchored on MXene surface were obtained using a simple solvothermal strategy. We prepared three samples (CaV 4 O 9 -MXene-0.1, CaV 4 O 9 -MXene-0.2, and CaV 4 O 9 -MXene-0.3) with different MXene contents based on the mass of MXene used (0.1 g, 0.2 g, and 0.3 g). Figures 1b-d and S1 displays scan electron microscope (SEM) images of MXene and CaV 4 O 9 -MXene materials. As can be seen from Figure 1c, CaV 4 O 9 nanosheets grew uniformly on the MXene surface and were able to preserve the layer structure of MXene; the morphology can enlarge the layer intervals of MXene and increase the surface area and sites for ion storage. In addition, CaV 4 O 9 consists of numerous interleaved ultra-thin nanosheets forming a spherical flower structure, which may be due to the absence of MXene substrate. In contrast, composites with a higher concentration of MXene exhibited a stacked layered structure and full coating ( Figure S1a-d).

Structure Characterization
The morphology of CaV 4 O 9 -MXene-0.1 was investigated using high-resolution transmission electron microscopy (HRTEM). As shown in Figure 1e-g, it appears that the presence of ultrathin CaV 4 O 9 nanosheets uniformly anchored on Ti 3 C 2 T x layers. The crystalline lattice of CaV 4 O 9 -MXene-0.1 can be clearly seen in Figure 1f. The crystal lattice distance was 0.24 nm, indexed to the (310) crystal plane of CaV 4 O 9 [26]. Energy dispersive X-ray spectroscopy (EDS) element mapping further revealed the uniform distribution of calcium, carbon, fluorine, titanium, vanadium, and oxygen elements in CaV 4 O 9 -MXene-0.1 material (Figure 1g). The morphology of CaV4O9-MXene-0.1 was investigated using high-resolution transmission electron microscopy (HRTEM). As shown in Figure 1e-g, it appears that the presence of ultrathin CaV4O9 nanosheets uniformly anchored on Ti3C2Tx layers. The crystalline la ice of CaV4O9-MXene-0.1 can be clearly seen in Figure 1f. The crystal la ice distance was 0.24 nm, indexed to the (310) crystal plane of CaV4O9 [26]. Energy dispersive X-ray spectroscopy (EDS) element mapping further revealed the uniform distribution of calcium, carbon, fluorine, titanium, vanadium, and oxygen elements in CaV4O9-MXene-0.1 material (Figure 1g).
To explore the microstructure of the CaV4O9-MXene cathode material synthesized under different amounts of MXene, XRD pa erns were recorded (Figure 2a). From the XRD pa erns, we found that the characteristic peaks of composites appeared at 29.8°, 33.7°, 43.5°, and 48.8°, respectively, and no impurity was detected, showing that CaV4O9 is a purified phase [35]. The composite showed weak MXene diffraction peaks compared with pure MXene, which may be due to the low MXene content and the coating of CaV4O9 nanosheets on the MXene surface. X-ray photoelectron spectroscopy (XPS) was used to analyze the surface chemical properties and chemical states of CaV4O9-MXene-0.1. Based on the full spectrum of CaV4O9-MXene-0.1, peaks at 346.8 eV, 517.4 eV, and 531.0 eV correspond to Ca 2p, V 2p, and O 1s, respectively ( Figure S2). As shown in Figure 2b, the Ca 2p spectrum showed two types of bands at 347.5 eV and 350.8 eV [36]. In the highresolution V 2p spectrum (Figure 2c), CaV4O9-MXene-0.1 showed the characteristic peak a ributed to V 4+ at 515.7 and 531.4 eV, and the dominant V 5+ signal at 517.2 and 529.7 eV [37]. The surface area of CaV4O9-Mxene-0.1 was measured using the N2 To explore the microstructure of the CaV 4 O 9 -MXene cathode material synthesized under different amounts of MXene, XRD patterns were recorded ( Figure 2a). From the XRD patterns, we found that the characteristic peaks of composites appeared at 29.8 • , 33.7 • , 43.5 • , and 48.8 • , respectively, and no impurity was detected, showing that CaV 4 O 9 is a purified phase [35]. The composite showed weak MXene diffraction peaks compared with pure MXene, which may be due to the low MXene content and the coating of CaV 4 O 9 nanosheets on the MXene surface. X-ray photoelectron spectroscopy (XPS) was used to analyze the surface chemical properties and chemical states of CaV 4 O 9 -MXene-0.1. Based on the full spectrum of CaV 4 O 9 -MXene-0.1, peaks at 346.8 eV, 517.4 eV, and 531.0 eV correspond to Ca 2p, V 2p, and O 1s, respectively ( Figure S2). As shown in Figure 2b, the Ca 2p spectrum showed two types of bands at 347.5 eV and 350.8 eV [36]. In the high-resolution V 2p spectrum (Figure 2c), CaV 4 O 9 -MXene-0.1 showed the characteristic peak attributed to V 4+ at 515.7 and 531.4 eV, and the dominant V 5+ signal at 517.2 and 529.7 eV [37]. The surface area of CaV 4 O 9 -Mxene-0.1 was measured using the N 2 adsorption/desorption curves ( Figure 2d). The results showed that the specific surface area of the composite was 20.315 m 2 g −1 due to the uniform coating of CaV 4 O 9 nanoflakes on the surface of MXene. The adsorption and desorption curves showed that the CaV 4 O 9 -MXene-0.1 composite had H 3 hysteresis loops in the type IV isotherm [6,38], indicating mesoporous properties of the composites. adsorption/desorption curves (Figure 2d). The results showed that the specific surface area of the composite was 20.315 m 2 g −1 due to the uniform coating of CaV4O9 nanoflakes on the surface of MXene. The adsorption and desorption curves showed that the CaV4O9-MXene-0.1 composite had H3 hysteresis loops in the type IV isotherm [6,38], indicating mesoporous properties of the composites.

Electrochemical Performance
To identify the distinctive structural benefits of CaV4O9-MXene material, electrochemical tests were carried out. Figure S3 shows the galvanostatic chargedischarge (GCD) curve of MXene at a current density of 0.1 A g −1 . As can be seen, the stable discharge capacity was only 39 mAh g −1 , and after compositing with CaV4O9, a higher specific capacity was obtained (Figures 3a and S4). By comparing the composites with different proportions, CaV4O9-MXene-0.1 achieved a higher specific discharge capacity of 274.3 mAh g −1 after 10 cycles, which means that the composite may be helpful to improve the zinc storage capacity of CaV4O9-MXene material. Notably, the low Coulombic efficiencies of the first cycle correspond to electrolyte decomposition and SEI film formation [39]. The rate performance of the MXene and CaV4O9-MXene cathode is compared in Figure 3b at different current densities from 0.1 to 2 A g −1 . Taking CaV4O9-MXene-0.1 as an example, the discharge capacities of 271.6 mAh g −1 , 267.2 mAh g −1 , 254.2 mAh g −1 , 232.1 mAh g −1 , and 207.5 mAh g −1 can be achieved at current densities of 0.1, 0.2, 0.5, 1, and 2 A g −1 , respectively. While the current recovered back to 0.1 A g −1 , the reversible capacity was covered to 260.1 mAh g −1 , corresponding to a capacity retention of 95.8%. Similarly, for CaV4O9-MXene-0.2 and CaV4O9-MXene-0.3, as the current rate recovered after 50 cycles to 0.1 A g −1 , the discharge capacity was 159.6 and 202.6 mAh g −1 , respectively. Obviously, compared with pure MXene, the composite material exhibited improved electrochemical properties, among which the performance of CaV4O9-MXene-0.1 was the best, in accordance with the results of galvanostatic charge/discharge test.

Electrochemical Performance
To identify the distinctive structural benefits of CaV 4 O 9 -MXene material, electrochemical tests were carried out. Figure S3 shows the galvanostatic charge-discharge (GCD) curve of MXene at a current density of 0.1 A g −1 . As can be seen, the stable discharge capacity was only 39 mAh g −1 , and after compositing with CaV 4 O 9 , a higher specific capacity was obtained (Figures 3a and S4). By comparing the composites with different proportions, CaV 4 O 9 -MXene-0.1 achieved a higher specific discharge capacity of 274.3 mAh g −1 after 10 cycles, which means that the composite may be helpful to improve the zinc storage capacity of CaV 4 O 9 -MXene material. Notably, the low Coulombic efficiencies of the first cycle correspond to electrolyte decomposition and SEI film formation [39]. The rate performance of the MXene and CaV 4 O 9 -MXene cathode is compared in Figure 3b at different current densities from 0.1 to 2 A g −1 . Taking CaV 4 O 9 -MXene-0.1 as an example, the discharge capacities of 271.6 mAh g −1 , 267.2 mAh g −1 , 254.2 mAh g −1 , 232.1 mAh g −1 , and 207.5 mAh g −1 can be achieved at current densities of 0.1, 0.2, 0.5, 1, and 2 A g −1 , respectively. While the current recovered back to 0.1 A g −1 , the reversible capacity was covered to 260.1 mAh g −1 , corresponding to a capacity retention of 95.8%. Similarly, for CaV 4 O 9 -MXene-0.2 and CaV 4 O 9 -MXene-0.3, as the current rate recovered after 50 cycles to 0.1 A g −1 , the discharge capacity was 159.6 and 202.6 mAh g −1 , respectively. Obviously, compared with pure MXene, the composite material exhibited improved electrochemical properties, among which the performance of CaV 4 O 9 -MXene-0.1 was the best, in accordance with the results of galvanostatic charge/discharge test.  In comparison with pure MXene, all composites displayed improved cycling properties as shown in Figure 3e. When the current density was 0.1 A g −1 , the specific discharge capacity of CaV4O9-MXene-0.1 remained at 185.1 mA h g −1 after 100 cycles. We continued to carry out the cycle performance test at 0.2 A g −1 . After 100 cycles, the specific discharge capacity was still 117.4 mA h g −1 . When we used a higher current density of 0.5 A g −1 , the specific discharge capacity was 73.2 mA h g −1 after 300 cycles. This shows that the CaV4O9-MXene composite exhibits good stability. The electrolyte ion and electron transport characteristics of MXene and the CaV4O9-MXene composite were further analyzed using electrochemical impedance spectroscopy (EIS) (Figure 3c). The semicircle observed in the high frequency area responds to the charge transfer (Rct) impedance at the interface [40]. The Rct value of CaV4O9-MXene was significantly lower than that of MXene, indicating faster charge transfer in electrochemical reactions. For comparison, CaV4O9-MXene-0.1 showed smaller impedance and be er conductivity, indicating the faster kinetics characteristics of CaV4O9-MXene over MXene. The Ragone plots are shown in Figure 3d; the delivered specific energy and power density of CaV4O9-MXene was In comparison with pure MXene, all composites displayed improved cycling properties as shown in Figure 3e. When the current density was 0.1 A g −1 , the specific discharge capacity of CaV 4 O 9 -MXene-0.1 remained at 185.1 mA h g −1 after 100 cycles. We continued to carry out the cycle performance test at 0.2 A g −1 . After 100 cycles, the specific discharge capacity was still 117.4 mA h g −1 . When we used a higher current density of 0.5 A g −1 , the specific discharge capacity was 73.2 mA h g −1 after 300 cycles. This shows that the CaV 4 O 9 -MXene composite exhibits good stability. The electrolyte ion and electron transport characteristics of MXene and the CaV 4 O 9 -MXene composite were further analyzed using electrochemical impedance spectroscopy (EIS) (Figure 3c). The semicircle observed in the high frequency area responds to the charge transfer (Rct) impedance at the interface [40]. The Rct value of CaV 4 O 9 -MXene was significantly lower than that of MXene, indicating faster charge transfer in electrochemical reactions. For comparison, CaV 4 O 9 -MXene-0.1 showed smaller impedance and better conductivity, indicating the faster kinetics characteristics of CaV 4 O 9 -MXene over MXene. The Ragone plots are shown in Figure 3d; the delivered specific energy and power density of CaV 4 [43].
To determine the reaction mechanism, cyclic voltammetry (CV) curves were obtained in initial several cycles at a scan rate of 0.05 mV s −1 in the voltage range of 0.2-1.6 V. As shown in Figure 4a, the CV curve showed two pairs of distinct redox peaks. The oxidation peaks were located at 0.671 V and 1.001 V, and the reduction peaks were at 0.577 V and 0.94 V, respectively. It is proved that there is a two-step reaction process in the insertion/extraction process of Zn 2+ [44]. In the following scan, the CV curve had a good degree of coincidence, and the redox peak of CaV 4 O 9 -MXene-0.1 was almost unchanged, which proves good stability and reversibility. At high current density (Figure 4b), the CaV 4 O 9 -MXene-0.1 still exhibited an excellent capacity retention. When the current density ranged from 0.1 to 7 to 0.1 A g −1 , the CaV 4 O 9 -MXene-0.1 electrode showed excellent rate performance, and CaV 4 O 9 -MXene-0.1 provided higher reversible capacities of 246.6, 185.5, 164.1, 137.4, and 130.2 mA h g −1 at 0.1, 1, 2, 5, and 7 A g −1 , respectively. When the current gradually recovered to 0.1 A g −1 , 77.1% of the initial capacity was restored, indicating that MXene can synergistically accelerate kinetics and enhance the rate capability. Figure 4c is the comparison of cycle performance at a current density of 1 A g −1 . The specific discharge capacity of CaV 4 O 9 -MXene-0.1 in the first cycle was 221.6 mA h g −1 , which can be stably cycled for 2000 times. The cycling performances of the CaV 4 O 9 -MXene-0.2 and CaV 4 O 9 -MXene-0.3 composites showed obvious attenuation, and CaV 4 O 9 -MXene-0.1 showed the best cycling stability. The rate and cycling performance of CaV 4 O 9-MXene were superior to many reported vanadium-based cathodes (Table S1).  [43].
To determine the reaction mechanism, cyclic voltammetry (CV) curves were obtained in initial several cycles at a scan rate of 0.05 mV s −1 in the voltage range of 0.2-1.6 V. As shown in Figure 4a, the CV curve showed two pairs of distinct redox peaks. The oxidation peaks were located at 0.671 V and 1.001 V, and the reduction peaks were at 0.577 V and 0.94 V, respectively. It is proved that there is a two-step reaction process in the insertion/extraction process of Zn 2+ [44]. In the following scan, the CV curve had a good degree of coincidence, and the redox peak of CaV4O9-MXene-0.1 was almost unchanged, which proves good stability and reversibility. At high current density (Figure 4b), the CaV4O9-MXene-0.1 still exhibited an excellent capacity retention. When the current density ranged from 0.1 to 7 to 0.1 A g −1 , the CaV4O9-MXene-0.1 electrode showed excellent rate performance, and CaV4O9-MXene-0.1 provided higher reversible capacities of 246.6, 185.5, 164.1, 137.4, and 130.2 mA h g −1 at 0.1, 1, 2, 5, and 7 A g −1 , respectively. When the current gradually recovered to 0.1 A g −1 , 77.1% of the initial capacity was restored, indicating that MXene can synergistically accelerate kinetics and enhance the rate capability. Figure 4c is the comparison of cycle performance at a current density of 1 A g −1 .
The specific discharge capacity of CaV4O9-MXene-0.1 in the first cycle was 221.6 mA h g −1 , which can be stably cycled for 2000 times. The cycling performances of the CaV4O9-MXene-0.2 and CaV4O9-MXene-0.3 composites showed obvious a enuation, and CaV4O9-MXene-0.1 showed the best cycling stability. The rate and cycling performance of CaV4O9-MXene were superior to many reported vanadium-based cathodes (Table S1).

Electrochemical Kinetics
To further reveal the electrochemical kinetics of the zinc ion diffusion process and the contribution of pseudo capacitance behavior of the CaV4O9-MXene-0.1 electrode, CV curves in the voltage range of 0.2-1.6 V at different scan rates are provided in Figure 5a. All CV curves showed two pairs of redox peaks with similar shape, which correspond to the voltage plateau of the charge-discharge curves and can be a ributed to a two-step

Electrochemical Kinetics
To further reveal the electrochemical kinetics of the zinc ion diffusion process and the contribution of pseudo capacitance behavior of the CaV 4 O 9 -MXene-0.1 electrode, CV curves in the voltage range of 0.2-1.6 V at different scan rates are provided in Figure 5a. All CV curves showed two pairs of redox peaks with similar shape, which correspond to the voltage plateau of the charge-discharge curves and can be attributed to a two-step reaction Nanomaterials 2023, 13, 1536 8 of 11 of Zn 2+ in the CaV 4 O 9 -MXene lattice. Generally, the relationship between peak current (i) and scan rate (v) can be expressed as: where i and v are current and scan rate, and a and b are variable parameters. In Formula (2), the slopes of log (i) and log (v) can be used to calculate the value of b, which can analyze the charge storage mechanism during electrochemical reactions [45]. When the electrode process is controlled by diffusion, the value of b is 0.5, manifesting as the response current proportionating to the square root of the voltage scan rate. When the electrode process is controlled by capacitance, the value of b is one. As shown in b, the b values of peaks P1, P2, P3, and P4 are 0.83, 0.97, 0.88, and 0.73, respectively, demonstrating that the electrode is mainly controlled by the pseudo capacitance and, thus, has a fast zinc storage performance.
In addition, the potential-dependent capacitive behavior is identified by the previously reported method: where k is a constant and the responding current (i) at a given voltage (V) is quantified as k 1 ν (capacitive effect) and k 2 ν 1/2 (diffusion control behavior) [11]. The equation can be transferred into the format below: Nanomaterials 2023, 13, x FOR PEER REVIEW 8 of 12 reaction of Zn 2+ in the CaV4O9-MXene la ice. Generally, the relationship between peak current (i) and scan rate ( ) can be expressed as: where and are current and scan rate, and and are variable parameters. In Formula (2), the slopes of log ( ) and log ( ) can be used to calculate the value of , which can analyze the charge storage mechanism during electrochemical reactions [45]. When the electrode process is controlled by diffusion, the value of is 0.5, manifesting as the response current proportionating to the square root of the voltage scan rate. When the electrode process is controlled by capacitance, the value of is one. As shown in Figure  5b, the b values of peaks P1, P2, P3, and P4 are 0.83, 0.97, 0.88, and 0.73, respectively, demonstrating that the electrode is mainly controlled by the pseudo capacitance and, thus, has a fast zinc storage performance. In addition, the potential-dependent capacitive behavior is identified by the previously reported method: where is a constant and the responding current ( ) at a given voltage (V) is quantified as ν (capacitive effect) and ν 1/2 (diffusion control behavior) [11]. The equation can be transferred into the format below:  Therefore, it can be analyzed based on the linear relationship between i/v 1/2 and v 1/2 . From Figure 5c, the contribution of pseudo capacitance was about 54.7% at a scan speed of 0.5 mV s −1 . As shown in Figure 5d, the contribution rate of pseudo capacitance at different scan rates was obtained. When the scan rate was 0.1, 0.2, 0.5, 1, 2, and 5 mV s −1 , the contribution was 49.6, 53.4, 54.7, 57.4, 65.4, and 97.5%, respectively. The high pseudo capacitance control is helpful to accelerate the charging and discharging rate. A high percentage of capacitive behavior can bring fast response kinetics of the electrodes, which contributes to its high-rate properties. Furthermore, the contact angle of CaV 4 O 9 -MXene-0.1 after dropping with 2 µL electrolyte reached 101.94 • immediately, and subsequently reduced to 26.99 • after 10 s, indicating good wettability (Figure 5e). This facilitated the reduction in resistance and fast Zn 2+ transfer.

Conclusions
In summary, we designed and synthesized a CaV 4 O 9 -MXene composite through an efficient solvothermal strategy. CaV 4 O 9 nanosheets were uniformly anchored on the layer and surface of MXene, which expanded the MXene layer. The expanded specific surface area provided abundant active sites for Zn 2+ storage, and the addition of MXene enhanced the electrical conductivity. Benefiting from the synergistic effect of enhanced electron/ion transfer and a unique layered structure, the as-obtained CaV 4 O 9 -MXene exhibited an excellent cycling and rate performance when used as a cathode for AZIBs. Specifically, the CaV 4 O 9 -MXene-0.1 cathode exhibited a highly reversible capacity of 107.6 mAh g −1 after 2000 cycles at a current density of 1 A g −1 . It showed good rate performance with a specific capacity of 142.9 mAh g −1 , even at a high current density of 7 A g −1 . Additionally, it had excellent structural stability, high energy density, and power density (888.79 Wh kg −1 at 325.56 W kg −1 ). This work provides a method for the design of high-performance electrode materials featuring layered MXene and vanadium-based materials, and creates a novel pathway for the application of low-cost ZIBs systems.  Table S1: The comparison of the rate and cycling performance of vanadium-based cathodes in aqueous ZIBs. References [46][47][48][49][50][51][52][53] are cited in the supplementary materials.

Data Availability Statement:
The data presented in this study are available on request from the corresponding author.

Conflicts of Interest:
The authors declare no conflict of interest.